Kuumbwa Kwemakemikari
Alloy C2000 kemikari yakagadzirwa
Iyo kemikari yeHastelloy C-2000 inoratidzwa mutafura pazasi:
| Element | Min % | Max% |
|---|---|---|
| Cr | 22.00 | 24.00 |
| Mo | 15.00 | 17.00 |
| Fe | - | 3.00 |
| C | - | 0.01 |
| Si | - | 0.08 |
| Co | - | 2.00 |
| Mn | - | 0.50 |
| P | - | 0.025 |
| S | - | 0.01 |
| Cu | 1.30 | 1.90 |
| Al | - | 0.50 |
| Ni | bal |
Alloy Details
Hastelloy C-2000 density, melting point, coefficient yekuwedzera, uye modulus ye elasticity inoratidzwa mutafura iri pasi apa:
| Density | Melting Point | Coefficient of Kuwedzera | Modulus yeRigidity | Modulus yeElasticity |
|---|---|---|---|---|
| 8.5 g/cm³ | 1399 °C | 12.4 μm/m °C (20 – 100 °C) | 79 kN/mm² | 206 kN/mm² |
| 0.307 lb/in³ | 2550 °F | 6.9 x 10-6mukati/mu°F (70 – 212 °F) | 11458 ksi | 29878 ksi |
Kupisa kupisa kwezvikamu zvakapedzwa
Alloy C2000 kemikari yakagadzirwa
Iyo yakajairika kupisa kurapwa kweHastelloy C-2000:
| Condition sekupihwa neAWI | Type | Tembiricha | Nguva | Kutonhodza |
|---|---|---|---|---|
| Annealed kana Spring Temper | Kushungurudzika Kuderedza | 400 - 450 °C (750 - 840 °F) | 2 Hr | Air |
Properties
Iyo yakajairwa michina zvimiro zveHastelloy C-2000:
| Annealed | ||
|---|---|---|
| Approx.tensile simba | <1000 N/mm² | <145 ksi |
| Approx.kushanda tembiricha zvichienderana nemutoro ** uye nharaunda | -200 kusvika +400 °C | -330 kusvika +750 °F |
| Spring Temper | ||
|---|---|---|
| Approx.tensile simba | 1300 - 1600 N/mm² | 189 – 232 ksi |
| Approx.kushanda tembiricha zvichienderana nemutoro ** uye nharaunda | -200 kusvika +400 °C | -330 kusvika +750 °F |